| GRADE |
W6 | W10 | W12 | W15 | W25 | CR-A | |
| Color | black | black | black | black | black | black | |
| Elongation Break (%) ±10% | 555 | 430 | 460 | 367 | 407 | 465 | |
| Tensile Strength (kg/cm2) ±10% | 9 | 9.3 | 13.5 | 15.2 | 22.6 | 11.5 | |
| Tear Strength (kg/cm)±10% | 2.9 | 3 | 4.4 | 4.5 | 6.4 | 3.5 | |
| Hardness (Type C) ±2° | 8 | 8 | 11 | 13 | 23 | 9 | |
| Hardness (Durometer "00")±5° | 22 | 25 | 33 | 37 | 53 | 29 | |
| Density (g/cm3)±0.02 | 0.18 | 0.14 | 0.22 | 0.23 | 0.38 | 0.20 | |
| Modulus at 200% (kg/cm2) | 2-4 | 3-5 | 3-5 | 6-8 | 8-10 | 4-5 | |
| Lamination Sheet Size (inch) ±5% | 50" x 81" 50" x 130" |
50" x 130" | 48" x 120" | 50" x 130" | 42" x 48" | 47" x 128" | |
| GRADE | NS-6 | NS-10 | NS-12 | EPDM-B | EPDM-W28 | EPDM-W30 | |
| Color |
black | black | black | black | Grey | Grey | |
| Elongation Break (%) ±10% | 250 | 270 | 250 | 250 | 350 | 500 | |
| Tensile Strength (kg/cm2) ±10% | 4 | 5 | 6 | 8 | 10 | 9 | |
| Tear Strength (kg/cm)±10% | 1.8 | 1.8 | 2 | 3 | 8 | 4 | |
| Hardness (Type C) ±2° | 8 | 10 | 12 | 15 | 25 | 28 | |
| Hardness (Durometer "00")±5° | 18 | 22 | 25 | 30 | 50 | 54 | |
| Density (g/cm3) | 0.16±0.02 | 0.18±0.02 | 0.20±0.02 | 0.22±0.02 | 0.40±0.02 | 0.20±0.02 | |
| Modulus at 200% (kg/cm2) | 2-4 | 3-5 | 3-5 | 4-6 | 8-10 | 4-5 | |
| Lamination Sheet Size (inch) ±5% | 50" x 128" | 50" x 128" | 48" x 120" | 40" x 100" | 44" x 114" | 44" x 114" | |
* NS = 30% Neoprene / 70% SBR
* EPDM Rubber = Ethylene Propylene Diene Monomer (for higher/ lower temperature applications)
* CR-UNO provides this information as a technical service. Information provided as a result of CR-UNO's own technical analysis and testing is accurate to the extent of our knowledge and ability, using the standardized method and procedure. Each user of these products, or information, should perform their own tests to determine the safety, fitness and suitability of the products, or combination of products, for any foreseeable purposes, applications and uses by the user and by any third party to which the user may convey the products. CR-UNO doesn't guarantee that the user will obtain the same results as published above specification. The data and information are provided as a technical service, and the data and information are subject to change without notice.
| CR CR-A NS |
100% Neoprene 100% Neoprene(Extra Stretch) Neoprene / SBR Blend |
| Natural Smoothskin Sharkskin MicroGrid |
Smooth, Dull and Slightly Tacky Smooth, Bright and Less Tacky Large Grid Pattern Very Fine Grid Pattern |
| Nylon / Polyester Visa Loop Plush Loop (long & short) Spandex Wickable Terry Cloth Opelon UBL Domestic UBL Pique Special Functional Fabrics |
Standard Neoprene Covering Value Priced Hook Compatible Fabic Alternative Value Priced Hook Compatible Fabric Maximum Stretch, Silky Feel Specially Treated for Comfort High End Hook Compatible Fabric - High Cycle Life High End Hook Compatible Fabric - High Cycle Life Textured Nylon Anti-bacterial, Cool, Breathable, Accumulation of Heat (THERMAL) , ect. |
| Metric Measure 1.5 mm 2.0 mm 3.0 mm 4.0 mm 5.0 mm 6.0 mm |
English Equivalent 1/16 inch 5/64 inch 1/8 inch 5/32 inch 3/16 inch 1/4 inch |
| Standard: Special Order: Custom Colors: |
Black, Beige, Royal & Navy. Red, Gray, Charcoal, Silver, Purple, Jade, Green and Burgundy Available on Volume Orders |
| 1.5 - 2.0 mm 3.0 - 4.0 mm 5.0 - 6.0 mm |
10 - 15 Sheets per Carton 8 - 10 Sheets per Carton 6 - 7 Sheets per Carton |
| 1.0 mm to 31 mm (1/16 inch to 1-1/8 inch) Perforation process available. | |
|
Laminated sheet thickness with fabric finishes : Split sheet, natural unfinished both sides : Full bun thickness : |
1.5 to 12 mm 1.0 to 30 mm. 35 mm |